LEGHE

LEGA UNIVERSALE SUPER ELASTICA CON ELEVATO LIMITE ELASTICO INDICATA PER TUTTI I TIPI DI PROTESI SCHELETRICA 

COLORE BIANCO PD 24.98 AG 70.00 ZN 03.00 IN 02.00 PESO SPECIFICO 10.5 MODULO ELASTICO 83 GPA

COLORE BIANCO AU 15.00 PD 52.20 AG 21.50 C.E.T. 14.5-14.7 PESO SPECIFICO 11.6 MODULO ELASTICO 130 GPA

LEGA PER SCHELETRICA CON OTTIME PROPRIETA' DI RESISTENZA ED ELASTICITA'

LEGA NON PREZIOSA PER SCHELETRATI Co(64),Cr(28),Mo(6),Fe(<1),Mn(<1),Si(<1),C(<1) DUREZZA VICKERS 380HV ELONGAZIONE 10%

COLORE BIANCO AU 02.00 PD 75.90 CU 10.00 SN 06.00 C.E.T. 13.8-14.1 PESO SPECIFICO 10.7 MODULO ELASTICO 138 GPA

CR 22.00 NI 54.00 MO 09.00 FE 04.00 CET 14.1-14.4 PESO SPECIFICO 8.6 MODULO ELASTICO 160 GPA

TIPO 4 NOBLE COLORE BIANCO AU 1% PD 57.29% AG 29% IN 11% SN 1% GA 0.5% C.E.T. 14.3 - 14.6 OSSIDAZIONE 650°C - 1040°C 10 MIN SENZA VUOTO PUNTO DI FUSIONE 1430°C PESO SPECIFICO 11.3

LEGA GIALLA NON PREZIOSA PER MODELLI DIMOSTRATIVI NON CERAMIZZABILE! Cu 78.8 Al 8.8 Ni 4.9 Fe 3.9 Zn 2.7 Mn <1.0

COLORE BIANCO PD 60.55 AG 28.10 SN 02.50 IN 06.60 GA 02.10 C.E.T. 14.4-14.7 PESO SPECIFICO 11.2 MODULO ELASTICO 120 GPA

COLORE BIANCO PD 53.60 AG 37.50 SN 08.30 ZN 00.50 C.E.T. 14.9-15.1 PESO SPECIFICO 11 MODULO ELASTICO 137 GPA

LEGA NOBILE COLORE BIANCO RU 25 CO 40 CR 24 GA 11 C.E.T. 13.8-14.3 PESO SPECIFICO 9.0 MODULO ELASTICO 250

LEGA NOBILE ECONOMICA PT 20% CO 43.5% CR 29.3% MN <1 SI <1 C.E.T. 14.3 - 14.6 PESO SPECIFICO 9.45 PUNTO DI FUSIONE 1500°C