CO 59.0

CR 25.0

MO 4.0

W 10.0

MN 0.8

SI 1.0

N 0.2

CET 500°C - 13.8

TEMP.FUSIONE - 1550°C

MODULO ELASTICO - 200 GPA

DENSITA' - 8.8

DUREZZA - 320